Molybdenum Metal Crucibles

1.Foreign name Moly crucible
2.Density≥9.8g/cm3
3.Bright appearance
4.Production raw material Mo-1 molybdenum powder
5.Use temperature 1100℃~1800℃
6.Main applications metallurgical industry, rare earth industry, single crystal silicon, etc.

Send Inquiry

Product Introduction

The Mo-1 molybdenum powder is used to make the molybdenum crucible, which is employed at temperatures between 1100°C and 1700°C. Molybdenum crucibles are sintered and forged from the final material. In general, molybdenum crucibles are manufactured from pure molybdenum, which prevents the mixing of molten metal powders. Molybdenum metal crucibles have a density of more than 9.8 g/cm3 and their operating temperature is between 1100°C. Apart from tungsten crucibles in the metal melting industry, it is another good choice.

I Physical and chemical properties

1、 Purity: Mo≥99.95%.

2、 Density: ≥9.8g/cm3.

3、 Maximum application temperature environment: 1800℃.

II Production process

Powdered molybdenum Sieving, Blanking, Isostatic Pressing, Rough and Fine Turning, Medium Frequency Sintering, Presentation

Molybdenum Metal Crucibles equipment

III Uses

It is mainly used in the metallurgical industry, rare earth industry, monocrystalline silicon, solar energy, artificial crystals and mechanical processing.Due to its high melting point of 2610°C, molybdenum metal crucibles are widely used as core containers in industrial furnaces such as sapphire single crystal growth furnaces, quartz glass melting furnaces and rare earth smelting furnaces, where the working temperature environment is generally above 2000°C.The molybdenum crucible, with its high purity, high density, lack of internal fissures, accurate dimensions, smooth inner and outer walls, etc., is particularly suitable for sapphire single crystal development furnaces. plays a key role in the success rate of the seed crystal, the quality control of the drawn crystal, the de-crystalisation of the sticking pot and the service life of the sapphire crystal growth process.

Molybdenum Metal Crucibles applications

IV Types:

drawn parts, powder forming, turned molybdenum crucibles, molybdenum crucibles with lid, welded molybdenum crucibles, cast molybdenum crucibles. At the same time, molybdenum crucibles can be sintered in a vacuum furnace, which means a metallurgical process in which the molybdenum powder is heat-treated at its melting point to improve the strength of the molybdenum metal crucibles.